FILTER MEDIUMS
|
|
Filter elements TU BY 590339385.001-2005 are designed for
fine filtration of melts of ferrous (grey, ductile and high-duty
cast iron, high-carbon and manganese steels) and non-ferrous
materials when casting in disposable sand molds and chill.
The filter base is hard grid-type structure 1.2 mm thick,
size of filter cells: 1.5x1.5 mm; 2.0x2.0 mm (1.0x1.0 mm for
aluminum alloys) and heat resistance up to 16800C
more
...
|
6,0 rub./dm2
|
MODIFYING INSETS FOR CAST IRON
|
|
Modifying element TU BY 100229713.003-2005 is designed for
complex out-of-furnace fluid iron processing when casting.
The processing includes "late" (in casting mold)
fluid iron melt inoculation by modifying element and also
fine filtration by elements of fine cleaning. A Unique composition
of the additive and its insertion method provide powerful
grafitizing effect and different section structure equalization
of different-walled details and size-reduction of melt structure
constituents.
more
...
|
180 rub./kg
|
EXOTHERMAL INSETS
|
|
Exothermal insets TU BY 590339385.004-2008 are designed for
producing steel and cast iron in gating systems with casting
temperature of 14000C to 17000C. The
aim of use - elimination of casting waste due to defects of
shrinkage, risers specific quantity of metal reduction by
20% to 40% and respectively in-spec casting output increase.
The aim is achieved by local heating of fluid metal (up to
20000C), which slows the process of melt hardening
in risers part of the gating system and by creating extra
gas pressure on metal in exothermal reaction zone. The shape
of inset (cone passing into frustum of cone) was developed
specially for using it with and automated molding.
more
...
|
520 rub./kg
|
ADIABATIC INSET
|

|
Adiabatic insets TU BY 590339385.005-2008 are designed to
be used for producing large-size (bulky) casts of all sorts
of steel, cast iron and non-ferrous materials with casting
temperature up to 16500C for riser heat insulation
to increase solidification time in the feeding boss and considerably
rise its efficiecy. Using feed systems with adiabatic insets
has the aim of increasing in-spec casting output (by 10-15%)
because of decrease of specific quantity of metal of risers
(up to 30%) and decreasing power inputs and elimination of
cast waste due to shrinkage defects.
more
...
|
620 rub./kg
|
PREPARATIONS FOR TREATMENT OF ALLOYS ON
THE BASIS OF ALUMINIUM
|

|
Complex treatment of alloys with tableted preparations together
with flux compositions is an effective element of procedure
of decrease of oxides and hydrogen content in melt, high-quality
modifying of non-ferrous melts and solving other problems
more
...
|
from
10
rub./kg
|
If you are interested in introduction of highly effective processes
of treatment of cast irons and non-ferrous melts collaborators of
our enterprise are ready to render consulting and technical support
including a business-trip onto your enterprise with a test batch
of necessary materials. This service is given at a no cost.
With questions on all sorts of products manufactured by ODO "Beltechnolit"
apply to:
Post address and address of the registered office:
220043, Tolbukhina str. 4, room 46, Minsk
Phone/fax (1037517) 280-76-12, 260-47-67
WWW.BELTL.RU
UNN 100229713, OKPO 14744709
Contact person:
Chief engineer Shamov Michael Urievich
Ph./ f. +375 17 280 76 12
mob. +375 29 751 97 66
|